POLYPROPYLENE HOMOPOLYMER
EXTRUSION GRADE

HPP C30S

PARAMETERTEST METHODVALUEUNIT
Melt flow rate (230 °C, 2.16 kg)ISO 11336dg / min
DensityISO 11830.9g/cm3  
Flexural modulusISO 1781500N/mm2
Tensile strength yieldISO R 52734N/mm2
Elongation at yieldISO R 52713%
Izod Impact Strength (notched) at 23°CISO 1804kJ/m2
Hardness Shore DISO 86871Points
Vicat softening point (9.8 N)ISO 306/A155°C
H.D.T. (0.46 Mpa)ISO 75/B112°C
Accelerated oven ageing in air

(forced circulation) at 150 °C

ISO 4577360hours
APPLICATIONS

Instance in brush and broom filling and technical applications, monolayer or coextruded film for packaging, thin sheet for stationery folders and sheet for thermoforming