HIGH DENSITY POLYETHYLENE
PIPE EXTRUSION
HDPE EX3-80
| PARAMETER | TEST METHOD | VALUE | UNIT |
| Density | ISO 1183 | 0.945 | g/cc |
| MFI (190 °C /21.6Kg) | ISO 1133 | 12 | g/10 min |
| Tensile Stress | at Break; ISO 527 | 35.0 | MPa |
| Tensile Strength, Yield | ISO 527 | 22.0 | MPa |
| Elongation at Break | ISO 527 | >= 850 | % |
| Elongation at Yield | ISO 527 | 8.0 | % |
| Tensile Modulus | ISO 527 | 0.850 | GPa |
| Charpy Impact, Notched | ISO 179/1eA | 2.30 | J/cm² |
| Softening Point | ISO 306 | 67.0 | °C |
| Brittleness Temperature | ASTM D746-72 | >= -80.0 | °C |
| Melt Temperature | – | 190 – 220 | °C |
| Flexural Creep Modulus (4 Point, 1 Min) | DIN 19537-2 | 950 | MPa |
APPLICATIONS
Pipe extrusion PE 80 class, industrial and pressure pipe , gas pipe, drinking water pipe, relining, fittings